I-Liaocheng sihe ibonelela ngoluhlu olupheleleyo lweemveliso kwicandelo le-oyile negesi, kwaye yenye yezona marike zethu zibalulekileyo.Uya kufumana iityhubhu zethu zokusebenza eziphezulu zisetyenziswe ngempumelelo kwezinye iimeko ezindlongondlongo zolwandle kunye ne-downhole enkosi kwirekhodi yethu eqinisekisiweyo yokuhlangabezana neemfuno ezingqongqo zomgangatho we-oyile, igesi kunye nemizi-mveliso yamandla e-geothermal.
316L ityhubhu yomgca wokulawula
Ukuphucula iteknoloji iye yandisa uluhlu lweendlela apho ioli kunye negesi yegesi ingasetyenziswa khona, kwaye iiprojekthi ezikhulayo zifuna ukusetyenziswa kwexesha elide, ubude obuqhubekayo bemigca yokulawula insimbi engenasici.Ezi ziqeshwe kwiinkqubo ezahlukeneyo ezibandakanya ulawulo lwe-hydraulic, i-instrumentation, i-chemical injection, i-umbilicals kunye nokulawula ukuhamba.I-Fine Tubes ibonelela ngeemveliso kuzo zonke ezi zicelo, kunye nokunye, ukunciphisa iindleko zokusebenza kunye neendlela eziphuculweyo zokubuyisela abathengi bethu.
316L ityhubhu yomgca wokulawula
Enkosi kwinkqubela phambili kubuchwepheshe bomgca wolawulo lwetyhubhu, ngoku kutshiphu kwaye kulula ukudibanisa iivalvu zemingxuma ephantsi kunye neenkqubo zokutofa ngekhemikhali ezinamaqula akude kunye nesathelayithi, kumaqonga aphakathi azinzileyo nadadayo.Sinikezela ngeetyhubhu ezijiyileyo kwimigca yolawulo kwintsimbi engatyiwayo kunye ne-nickel alloys.
316L ityhubhu yomgca wokulawula
Idatha yoBugcisa
Iipropati zoomatshini
316L ityhubhu yomgca wokulawula
| Ukucaphuka | I-Anealed | Kuyabanda (malunga nama-20%) | ||||
|---|---|---|---|---|---|---|
| Izinto eziphathekayo | 316 | 316L | 316 | 316L | ||
| I-Tensile Rm | 75 | 70 | ksi (min) | 102-131 | ksi (min) | |
| I-Tensile Rm | 515 | 485 | MPa (min) | 700-900 | MPa (min) | |
| Rp 0.2% Isivuno | 30 | 27 | ksi (min) | 73-102 | ksi (min) | |
| Rp 0.2% Isivuno | 205 | 182 | MPa (min) | 500-700 | MPa (min) | |
| Ubude (2” okanye 4D gl) | 35 | % (imiz) | 40 | % (imiz) | ||
IiPropati zoBume beNdawo (Ubushushu beGumbi)
| Ubushushu obubodwa (0-100°C) | 500 | J.kg-1.°K-1 |
| I-Thermal Conductivity | 16.3 | Wm -1.°K-1 |
| Ukwandiswa kweThermal | 15.9 | μm/μm/°C |
| IModulus Elasticity | 193 | GPA |
| Ukuxhathisa koMbane | 7.4 | Ohm-cm |
| Ukuxinana | 7.99 | g/cm3 |
Ukudityaniswa kwemichiza (% ngokobunzima)
| 316 | 316L | |||
|---|---|---|---|---|
| Isiqalelo | Min | Max | Min | Max |
| C | - | 0.08 | - | 0.035 |
| Mn | - | 2 | - | 2 |
| Ni | 10 | 14 | 10 | 15 |
| Cr | 16 | 18 | 16 | 18 |
| Mo | 2 | 3 | 2 | 3 |
| S | - | 0.03 | - | 0.03 |
| Si | - | 1 | - | 1 |
| P | - | 0.045 | - | 0.045 |