Ukuqulunqwa kwemichiza
I-alloy C2000 ukwakheka kweekhemikhali
Ukwakhiwa kweekhemikhali zeHastelloy C-2000 kuboniswe kwitheyibhile engezantsi:
| Isiqalelo | Min % | Ubuninzi % |
|---|---|---|
| Cr | 22.00 | 24.00 |
| Mo | 15.00 | 17.00 |
| Fe | - | 3.00 |
| C | - | 0.01 |
| Si | - | 0.08 |
| Co | - | 2.00 |
| Mn | - | 0.50 |
| P | - | 0.025 |
| S | - | 0.01 |
| Cu | 1.30 | 1.90 |
| Al | - | 0.50 |
| Ni | bal |
Iinkcukacha zengxubevange
Ubuninzi beHastelloy C-2000, indawo yokunyibilika, i-coefficient yokwandiswa, kunye nemodyuli ye-elasticity iboniswe kwitheyibhile engezantsi:
| Ukuxinana | Indawo yokunyibilika | I-Coefficient yoKwandiswa | Modulus of Rigidity | Imodyuli yeElasticity |
|---|---|---|---|---|
| 8.5 g/cm³ | 1399 °C | 12.4 μm/m °C (20 – 100 °C) | 79 kN/mm² | 206 kN/mm² |
| 0.307 lb/in³ | 2550 °F | 6.9 x 10-6kwi/kwi°F (70 – 212 °F) | 11458 ksi | 29878 ksi |
Ukunyangwa kobushushu beendawo ezigqityiweyo
I-alloy C2000 ukwakheka kweekhemikhali
Unyango oluqhelekileyo lobushushu lweHastelloy C-2000:
| Imeko njengoko inikezelwe yi-AWI | Uhlobo | Ubushushu | Ixesha | Ukupholisa |
|---|---|---|---|---|
| I-Annealed okanye iSpring Temper | Nciphisa Uxinzelelo | 400 – 450 °C (750 – 840 °F) | 2 Hr | Umoya |
Iipropati
Iimpawu eziqhelekileyo zoomatshini beHastelloy C-2000:
| I-Anealed | ||
|---|---|---|
| Malunga.tensile strength | <1000 N/mm² | <145 ksi |
| Malunga.ubushushu bokusebenza ngokuxhomekeke kumthwalo** kunye nokusingqongileyo | -200 ukuya +400 °C | -330 ukuya +750 °F |
| Ubushushu baseNtwasahlobo | ||
|---|---|---|
| Malunga.tensile strength | 1300 – 1600 N/mm² | 189 – 232 ksi |
| Malunga.ubushushu bokusebenza ngokuxhomekeke kumthwalo** kunye nokusingqongileyo | -200 ukuya +400 °C | -330 ukuya +750 °F |
Ixesha lokuposa: Mar-14-2023