C	Cr	Ni	Fe	Mn	Si	Mo	Co	P	S	Ti	Nb + Ta	Al
≤ 0.1	20 – 23	≥ 58	≤ 5	≤ 0.5	≤ 0.5	8 – 10	≤ 1*	≤ 0.015	≤ 0.015	≤ 0.4	3.15 - 4.15	≤ 0.4

(ubunzima%)
*Ukuba kumisiwe

Ngokwe-ASTM B444, ASME SB444, AMS 5581

Imeko	Tensile strength	Unikeze Amandla	Elongation
	ubuncinane, ksi	ubuncinane, ksi	ubuncinane, %
IBanga loku-1	120	60	30
IBanga lesi-2	100	40	30

*Iipropathi zamandla aphezulu zinokubonelelwa kwimeko ebandayo eqinileyo.

I-incoloy 625 ityhubhu ejiyileyo ye-capillary

		70°F	200°F	400°F	600°F	800°F	1000°F
Ukuxinana	lbs/nge3	0.305	-	-	-	-	-
Ukwandiswa kweThermal	X10-6/°F	-	7.1	7.3	7.4	7.6	7.7
Imodyuli ye-elastic	103 ksi	30.1	29.6	28.7	27.8	26.9	25.7
Umlinganiselo wePoisson	-	0.278	0.28	0.286	0.29	0.295	-
I-Thermal Conductivity	Btu-in/h·ft2 · °F	68	75	87	98	109	139
Ubushushu obuthile	Btu/lb·°F	0.098	0.102	0.109	0.115	0.122	0.118
Unikeze Amandla	ksi	70	68	63	60	59	34
Tensile strength	ksi	140	134	130	129	129	88

I-incoloy 625 ityhubhu ejiyileyo ye-capillary

PROCESSDESCRIPTIONSteel MakingElectric Arc Furnace elandelwa yiVacuum Oxygen Decarburization (VOD) okanye Argon Oxygen Decarburization (AOD).Ukwenziwa kwemibhobhoConventional Seamless Cold Finished uMbhobho kunye neTube Manufacturing Process.Heat TreatmentAyinakuqiniswa ngonyango lobushushu.Unokubonelelwa kwimeko efakwe i-annealed, isisombululo se-annealed okanye ebandayo.Amandla aphezulu e-annealed condition asetyenziswa ngokuqhelekileyo kwiinkonzo ukuya kuthi ga kwi-1100 ° F, ngelixa isisombululo se-annealed condition sisetyenziswa kwizicelo ezingaphezulu kwe-1100 ° F.