Izicelo zeBakala 310/310S Stainless Steel
I-310 310S ityhubhu ejiyileyo/i-capillary tube
Usetyenziso oluQhelekileyo lweBakala 310/310S lusetyenziswa kwizitshizi zebhedi ezimanzi, ii-kilns, iityhubhu ezikhazimlayo, izixhoma zetyhubhu zokusulungekisa i-petroleum kunye nezibhoyila zomphunga, izinto zangaphakathi zokufaka igesi yamalahle, iimbiza zelothe, iibholiti ze-anchor, izitshisi kunye namagumbi okutsha, iimufflers amakhava annealing, saggers, izixhobo zokulungisa ukutya, izakhiwo cryogenic.
Iipropati zeBanga 310/310S iStainless Steel
I-310 310S ityhubhu ejiyileyo/i-capillary tube
La mabanga aqulethe i-25% yechromium kunye ne-20% ye-nickel, ezenza ukuba zixhathise kakhulu kwi-oxidation kunye ne-corrosion.IBanga lama-310S luhlobo olusezantsi lwekhabhoni, alufanelwanga kukukhubeka kunye nolwazelelelo enkonzweni.I-chromium ephezulu kunye nomxholo we-nickel ophakathi kwenza ezi zintsimbi zikwazi ukusetyenziswa ekunciphiseni i-sulfur atmospheres equkethe i-H2S.Zisetyenziswa kakhulu kwindawo ephakathi kwe-carburising atmosphere, njengoko zidibene nemo yepetrochemical.Kwiimeko ezinzima ngakumbi ze-carburising atmosphere kufuneka kukhethwe ezinye iialloyi ezixhathisa ubushushu.IBanga lama-310 alikhuthazwa ukuba lucime ulwelo rhoqo njengoko linengxaki yomothuko wobushushu.Ibakala lihlala lisetyenziswa kwizicelo ze-cryogenic, ngenxa yokuqina kwayo kunye nokunyanzeliswa kwamagnetic.
I-310 310S ityhubhu ejiyileyo/i-capillary tube
Ngokufana nezinye i-austenitic stainless steels, la mabanga awanakuqiniswa ngonyango lobushushu.Zinokuqiniswa ngumsebenzi obandayo, kodwa oku akufane kwenzeke.
IChemcial Composition of Grade 310/310S Stainless Steel
Ukwakhiwa kweekhemikhali zebakala 310 kunye nebakala 310S insimbi engenasici zishwankathelwa kule theyibhile ilandelayo.
I-310 310S ityhubhu ejiyileyo/i-capillary tube
Uluhlu loku-1.Ukwakheka kweekhemikhali % yebanga lama-310 kunye ne-310S yentsimbi engatyiwayo
| Ukuqulunqwa kwemichiza | 310 | 310S |
| Ikhabhoni | 0.25 ubuninzi | 0.08 ubuninzi |
| IManganese | 2.00 ubuninzi | 2.00 ubuninzi |
| Isilicon | 1.50 ubuninzi | 1.50 ubuninzi |
| Iphosphorus | 0.045 ubuninzi | 0.045 ubuninzi |
| Isulfure | 0.030 ubuninzi | 0.030 ubuninzi |
| Chromium | 24.00 - 26.00 | 24.00 - 26.00 |
| Nickel | 19.00 - 22.00 | 19.00 - 22.00 |
IiPropati zeMechanical zeBanga 310/310S iNtsimbi eNgatyiwayo
Iimpawu zomatshini zebakala 310 kunye nebakala 310S intsimbi stainless zishwankathelwe kule theyibhile ilandelayo.
Itheyibhile 2.Iimpawu zeMechanical zebakala 310/310S intsimbi engatyiwayo
| Iipropati zoomatshini | 310/ 310S |
| Grade 0.2 % Ubungqina boxinzelelo lweMPa (min) | 205 |
| Amandla Okuqina kweMPa (min) | 520 |
| Elongation % (min) | 40 |
| Ukuqina (HV) (max) | 225 |
IiPropati zeMzimba zeFerritic Stainless Steel
Iimpawu ezibonakalayo zebakala 310 kunye nebakala 310S intsimbi stainless zishwankathelwe kule theyibhile ilandelayo.
Itheyibhile 3.Iimpawu ezibonakalayo zebakala 310 / 310S insimbi engenasici
| Iipropati | at | Ixabiso | Iyunithi |
| Ukuxinana |
| 8,000 | Kg/m3 |
| Ukuqhuba koMbane | 25°C | 1.25 | I-%IACS |
| Ukuxhathisa koMbane | 25°C | 0.78 | Micro ohm.m |
| Imodyuli yeElasticity | 20°C | 200 | GPA |
| Shear Modulus | 20°C | 77 | GPA |
| Umlinganiselo wePoisson | 20°C | 0.30 |
|
| Ukunyibilika kweRnage |
| 1400-1450 | °C |
| Ubushushu obuthile |
| 500 | J/kg.°C |
| I-Relative Magnetic Permeability |
| 1.02 |
|
| I-Thermal Conductivity | 100°C | 14.2 | W/m.°C |
| I-Coefficient yoKwandiswa | 0-100°C | 15.9 | /°C |
| 0-315°C | 16.2 | /°C | |
| 0-540°C | 17.0 | /°C |