316L/S31603 intsimbi engatyiwa 7.0 * 0.3 mm yokutshintsha ubushushu

Inkcazelo emfutshane:

Ezi zakhiwo zichazwe kwiimveliso eziqengqelekayo (ipleyiti, icwecwe, kunye nekhoyili) kwi-ASTM A240/A240M.Iipropati ezifanayo kodwa zingafane zichazwe kwezinye iimveliso ezinjengombhobho kunye nebar kwiinkcukacha zazo.

Ukuqamba

316L/S31603 intsimbi engatyiwa 7.0 * 0.3 mm yokutshintsha ubushushu

Uluhlu loku-1.Ukuqulunqwa koluhlu lwe-316L yensimbi engenasici.

IBanga   C Mn Si P S Cr Mo Ni N
316L Min - - - - - 16.0 2.00 10.0 -
Max 0.03 2.0 0.75 0.045 0.03 18.0 3.00 14.0 0.10

 

Iipropati zoomatshini

316L/S31603 intsimbi engatyiwa 7.0 * 0.3 mm yokutshintsha ubushushu

Itheyibhile 2.Iimpawu zeMechanical ze-316L zensimbi engenasici.

IBanga I-Tensile Str (MPa) min Isivuno Str 0.2% Ubungqina (MPa) min Elong (% kwi-50 mm) min Ukuqina
Rockwell B (HR B) max Brinell (HB) max
316L 485 170 40 95 217

 

Iipropati Zomzimba

316L/S31603 intsimbi engatyiwa 7.0 * 0.3 mm yokutshintsha ubushushu

Itheyibhile 3.Iimpawu ezibonakalayo eziqhelekileyo ze-316-grade steels stainless.

IBanga Ubuninzi (kg/m3) I-Elastic Modulus (GPA) I-Mean Co-eff yoKwandiswa kweThermal (µm/m/°C) I-Thermal Conductivity (W/mK) Ubushushu obubodwa 0-100 °C (J/kg.K) Ukuxhathisa kwe-Elec (nΩ.m)
0-100 °C 0-315 °C 0-538 °C Kwi-100 °C Kwi-500 °C
316/L/H 8000 193 15.9 16.2 17.5 16.3 21.5 500 740

 

Uthelekiso lweNgcaciso yeBanga

316L/S31603 intsimbi engatyiwa 7.0 * 0.3 mm yokutshintsha ubushushu

Uluhlu lwesi-4.Iimpawu zeBanga le-316L yensimbi engenasici.

IBanga Inombolo ye-UNS Old British I-Euronorm Swedish SS I-JIS yaseJapan
BS En No Igama
316L S31603 316S11 - 1.4404 X2CrNiMo17-12-2 2348 SUS 316L

Iinkcukacha zeMveliso

Iithegi zeMveliso

Ezi zakhiwo zichazwe kwiimveliso eziqengqelekayo (ipleyiti, icwecwe, kunye nekhoyili) kwi-ASTM A240/A240M.Iipropati ezifanayo kodwa zingafane zichazwe kwezinye iimveliso ezinjengombhobho kunye nebar kwiinkcukacha zazo.

Ukuqamba

316L/S31603 intsimbi engatyiwa 7.0 * 0.3 mm yokutshintsha ubushushu

Uluhlu loku-1.Ukuqulunqwa koluhlu lwe-316L yensimbi engenasici.

IBanga C Mn Si P S Cr Mo Ni N
316L Min - - - - - 16.0 2.00 10.0 -
Max 0.03 2.0 0.75 0.045 0.03 18.0 3.00 14.0 0.10

 

Iipropati zoomatshini

316L/S31603 intsimbi engatyiwa 7.0 * 0.3 mm yokutshintsha ubushushu

Itheyibhile 2.Iimpawu zeMechanical ze-316L zensimbi engenasici.

IBanga I-Tensile Str (MPa) min Isivuno Str 0.2% Ubungqina (MPa) min Elong (% kwi-50 mm) min Ukuqina
Rockwell B (HR B) max Brinell (HB) max
316L 485 170 40 95 217

 

Iipropati Zomzimba

316L/S31603 intsimbi engatyiwa 7.0 * 0.3 mm yokutshintsha ubushushu

Itheyibhile 3.Iimpawu ezibonakalayo eziqhelekileyo ze-316-grade steels stainless.

IBanga Ubuninzi (kg/m3) I-Elastic Modulus (GPA) I-Mean Co-eff yoKwandiswa kweThermal (µm/m/°C) I-Thermal Conductivity (W/mK) Ubushushu obubodwa 0-100 °C (J/kg.K) Ukuxhathisa kwe-Elec (nΩ.m)
0-100 °C 0-315 °C 0-538 °C Kwi-100 °C Kwi-500 °C
316/L/H 8000 193 15.9 16.2 17.5 16.3 21.5 500 740

 

Uthelekiso lweNgcaciso yeBanga

316L/S31603 intsimbi engatyiwa 7.0 * 0.3 mm yokutshintsha ubushushu

Uluhlu lwesi-4.Iimpawu zeBanga le-316L yensimbi engenasici.

IBanga Inombolo ye-UNS Old British I-Euronorm Swedish SS I-JIS yaseJapan
BS En No Igama
316L S31603 316S11 - 1.4404 X2CrNiMo17-12-2 2348 SUS 316L